Epoxy-terminated polyester

ABSTRACT

An epoxy terminated polyester having the structure 
     
       
         
         
             
             
         
       
         
         
           
             wherein R 1 — is 
           
         
       
    
     
       
         
         
             
             
         
       
         
         
           
             G- is 
           
         
       
    
     
       
         
         
             
             
         
       
         
         
           
             j is 0 to 5, —R 2 — is a divalent organic group, —R 22 — is a divalent alkyl group, and —R 22 — is a divalent alkyl group.

Epoxy-terminated compounds are useful for a variety of purposes. For example, epoxy-terminated compounds may undergo chemical reactions either with themselves or with one or more co-reactant to form polymers that have high molecular weight and/or are crosslinked. Such polymers are often useful for one or more of a wide variety of purposes, such as, for example, as adhesives.

US 2008/0081883 describes polyester polyols that are reaction products of 2,5-furandicarboxylic acid and polyepoxides. It is desired to provide epoxy terminated compounds that react well with polyamines to form useful adhesive compositions, such as, for example, laminating adhesives. It is also desired to provide epoxy terminated compounds that have desirably low viscosity over the temperature range of from approximately 25° C. to approximately 70° C.

The following is a statement of the invention.

The first aspect of the present invention is an epoxy terminated polyester having the structure

R¹— is

G- is

j is 0 to 5, —R²— is a divalent organic group, —R²¹— is a divalent alkyl group, and —R²²— is a divalent alkyl group.

The following is a detailed description of the invention.

As used herein, the following terms have the designated definitions, unless the context clearly indicates otherwise.

An epoxy terminated compound is a compound that contains one or more structure I

A diepoxide is a compound having exactly two groups of structure I. A glycidyl ether terminated compound is a compound that contains one or more structure II

An ester linkage is the structure III

A polyester is a compound that has two or more ester linkages. A polyol is a compound that has two or more —OH groups. A diol is a compound that has exactly two —OH groups. A polyamine is a compound that has two or more amine groups; the amine groups may be primary or secondary or a mixture thereof. A diamine is a compound that has exactly two amine groups; a diamine may have two primary amine groups, two secondary amine groups, or one primary amine group and one secondary amine group. A dicarboxylic acid is a compound having exactly two —COOH groups.

An aliphatic group is a chemical group that contains only carbon and hydrogen atoms and that contains no aromatic rings. A cycloaliphatic group is an aliphatic group that contains one or more cyclic structures. An alkyl group is an aliphatic group that has no double bonds. Alkyl groups include, for example, monovalent and divalent alkyl groups such as, for example, methylene groups, methyl groups, ethylene groups, ethyl groups, and larger alkylene and alkyl groups. A cycloalkyl group is an alkyl group that contains one or more cyclic structures. An aromatic group is any group having an aromatic ring.

An aliphatic amine is an amine in which the nitrogen atom of each amine group is bonded to a carbon atom that is part of an aliphatic group. An aromatic amine is an amine in which the nitrogen atom of each amine group is bonded to a carbon atom that is part of an aromatic ring.

When a ratio is said herein to be X:1 or greater, it is meant that the ratio is Y:1, where Y is greater than or equal to X. For example, if a ratio is said to be 3:1 or greater, that ratio may be 3:1 or 5:1 or 100:1 but may not be 2:1. Similarly, when ratio is said herein to be W:1 or less, it is meant that the ratio is Z:1, where Z is less than or equal to W. For example, if a ratio is said to be 15:1 or less, that ratio may be 15:1 or 10:1 or 0.1:1 but may not be 20:1.

The composition of the present invention is an epoxy terminated polyester having structure IV

In structure IV, the two —R¹ groups may be identical or different. Each R¹ group has the structure V

The group —R²— is a divalent organic group having fewer than 50 carbon atoms. The group G- has the structure II defined herein above. The number j is 0 to 5. The group —R²¹— is a divalent alkyl group. The group —R²²— is a divalent alkyl group.

The composition of the present invention may also contain, in addition to one or more compounds having structure IV, one or more compounds having structure IVA

where —B¹— has the structure

—B²— has the structure

-Q- has the structure

—R²¹O—R²²_(j)

j is 0 to 5, and n is 1 to 6. The group —R²¹— is a divalent alkyl group. The group —R²²— is a divalent alkyl group.

Preferably, —R²— is a group having structure VI

The number p is 0 to 20. Preferably p is 0 to 10; more preferably 0 to 5. Each —R³—, each —R⁴—, and each —R⁵— is, independent of the other, a divalent organic group. Within a single —R²— group, if p is 2 or greater, the various —R³— groups may be identical to each other or different from each other. Within a single —R²— group, if p is 2 or greater, the various —R⁴— groups may be identical to each other or different from each other.

Preferably, —R³— is selected from one or more divalent aliphatic groups, one or more divalent aromatic hydrocarbon groups, or a mixture thereof. Among aliphatic groups, preferred are alkyl groups; more preferred are linear or branched alkyl groups; more preferred are linear alkyl groups. Among aliphatic groups, preferred are those with 1 or more carbon atoms; more preferred are those with 2 or more carbon atoms; more preferred are those with 3 or more carbon atoms. Among aliphatic groups, preferred are those with 12 or fewer carbon atoms; more preferred are those with 8 or fewer carbon atoms; more preferred are those with 6 or fewer carbon atoms. Among aliphatic groups, preferred is —CH₂CH₂CH₂CH₂—. Among aromatic groups, preferred are those with the structure

including mixtures of isomers; more preferred is

The groups that are suitable and preferred for —R⁵— are the same as those for —R³—. The group —R⁵— may be different from all of the —R³— groups, or —R⁵— may be the same as one or all of the —R³— groups.

Preferably, —R⁴— is either an aliphatic group or is an aliphatic ether group. An aliphatic ether group has the structure VII

—R⁸O—R⁹_(r)O—R¹⁰—  VII

where —R⁸— and —R⁹— (if present) and —R¹⁰— are aliphatic groups, and where r is 0 to 10. The groups —R⁸— and —R⁹— (if present) and —R¹⁰— may be identical or may be different from each other. When —R⁴— is an aliphatic ether group, the following preferences apply to —R⁸—, —R⁹— (if present), —R¹⁰—, and r. Preferably, —R⁸— and —R⁹— (if present) and —R¹⁰— are identical. Preferably —R⁸— and —R⁹— (if present) and —R¹⁰— are linear or branched alkyl groups. Preferably —R⁸— and —R⁹— (if present) and —R¹⁰— each have 4 or fewer carbon atoms; more preferably 3 or fewer carbon atoms; more preferably exactly 2 carbon atoms. Preferably, r is 0 to 10; more preferably 0 to 5; more preferably 0 to 2; more preferably zero. When —R⁴— is an aliphatic group, —R⁴— is preferably an alkyl group; more preferably a linear alkyl group. When —R⁴— is an aliphatic group, —R⁴— has 1 or more carbon atom. When —R⁴— is an aliphatic group, —R⁴— preferably has 6 or fewer carbon atoms; more preferably 4 or fewer carbon atoms; more preferably 3 or fewer carbon atoms; more preferably exactly 2 carbon atoms.

In some embodiments (herein called “mixed polyester” embodiments), p is greater than 1, and some of the —R³— groups are not identical to other —R³— groups. In some mixed polyester embodiments, —R²— has the structure VIII

The groups —R³— and —R⁴— and —R⁵— are as defined herein above, and q is 1 or higher. Preferably q is 0 to 9; more preferably 1 to 4. The suitable and preferable groups for —R⁶— are the same as those for —R⁴—. The suitable and preferable groups for —R⁷— are the same as those for —R³—. In some mixed polyester embodiments (herein called “MP1” embodiments), —R⁵— is identical to —R³—, —R⁶— is identical to —R⁴—, and —R⁷— is different from —R³—. In some MP1 embodiments, all the —R⁴— groups are identical to each other; in other MP1 embodiments, some —R⁴— groups are different from other —R⁴— groups. In some mixed polyester embodiments (herein called “MP2” embodiments), —R⁵— is identical to —R⁷—, —R⁶— is identical to —R⁴—, and —R⁷— is different from —R³—. In some MP2 embodiments, all the —R⁴— groups are identical to each other; in other MP2 embodiments, some —R⁴— groups are different from other —R⁴— groups.

Preferred embodiments are selected from the following:

-   -   (a) embodiments in which p=0;     -   (b) embodiments in which p is 1 or greater and in which all the         —R³— groups are identical to each other, all the —R⁴— groups are         identical to each other, and —R⁵— is identical to —R³—;     -   (c) MP1 embodiments; and     -   (d) MP2 embodiments;

In structure V, j is preferably 1 or more. In structure V, j is preferably 5 or less; more preferably 4 or less; more preferably 3 or less; more preferably 2 or less. In structure V, j is most preferably 1.

In structure V, —R²¹— is a divalent alkyl group. Preferably, —R²¹— has 2 or more carbon atoms; more preferably 3 or more carbon atoms. Preferably, —R²¹— has 6 or fewer carbon atoms; more preferably 5 or fewer carbon atoms; more preferably 4 or fewer carbon atoms. Most preferably, —R²¹— has 3 carbon atoms. Among embodiments in which —R²¹— has 3 carbon atoms, preferably —R²¹— is selected from structures XX, XXI, and XXII:

In some embodiments, a mixture of polyesters will be present in which one polyester will have —R²¹— that is one of XX, XXI, or XXII, and another polyester will be present in which —R²¹— is a different one of XX, XXI, or XXII.

In structure V, if j is 1 or more, the suitable and preferred structures for —R²²— are the same as those for —R²¹—. The group-R²²— may be the same as —R²¹— or different from —R²¹—. If j is 2 or more, each —R²²— may be the same as every other —R²²— or some —R²²— groups may be different from other —R²²— groups. Preferably, every —R²²— has the same number of carbon atoms as every other —R²²—. Preferably —R²¹— has the same number of carbon atoms as every —R²²— group. Preferably, every —R²²— has three carbon atoms. Preferably, at least one —R²²— has structure XXI or XXII.

The epoxide terminated polyesters of this invention will preferably have an Epoxide Equivalent Weight (EEW) of 275 or higher; more preferably 350 or higher; more preferably 400 or higher. The epoxide terminated polyesters of this invention will preferably have an Epoxide Equivalent Weight (EEW) of 3500 or lower; more preferably 2500 or lower; more preferably 2000 or lower. The number-average molecular weight of the epoxy terminated polyester of the present invention will preferably be 500 or higher; more preferably 1000 or higher. The number-average molecular weight of the epoxy terminated polyester of the present invention will preferably be 8000 or lower, more preferably 6000 or lower, and more preferably 3500 or lower.

It is useful to characterize the level of low molecular weight (≦1000 Daltons) species present in the composition of the present invention. The level of low molecular weight species is defined as the percentage by weight of species having molecular weight of less than or equal to 1000 Daltons, based on the total weight of the composition. The level of low molecular weight species is preferably 55% or less; more preferably 30% or less; more preferably 25% or less.

The composition of the present invention may be made by any method. A preferred method includes reacting at least one diepoxide with at least one dicarboxylic acid. The diepoxide has the structure IX

G-Q-G  IX

G- is defined as in structure V. Q is defined as in structure IVA. The dicarboxylic acid has the structure X

The group —R²— is defined as in structure IV. Sufficient amount of compound having structure IX is used so that the reaction produces compound having structure IV.

Preferred compounds of structure X have acid value (which is measured as described below) of 110 or higher; more preferably 120 or higher; more preferably 125 or higher. Preferred compounds of structure X have acid value of 260 or lower; more preferably 200 or lower; more preferably 175 or lower. Preferred compounds of structure X have molecular weight of 430 or higher; more preferably 560 or higher; more preferably 640 or higher. Preferred compounds of structure X have molecular weight of 1020 or lower; more preferably 940 or lower; more preferably 900 or lower. Mixtures of suitable Mixtures of suitable compounds of structure X are also suitable. are also suitable.

In the reaction of at least one diepoxide with at least one dicarboxylic acid, the stoichiometric ratio of epoxide groups to carboxylic acid groups will preferably be 3.1:1 or greater; more preferably 2.9:1 or greater; more preferably 2.7:1 or greater. The stoichiometric ratio of epoxide groups to carboxylic acid groups will preferably be 2:1 or less; more preferably 1.6:1 or less; more preferably 1.3:1 or less.

The reaction of diepoxide with dicarboxylic acid is optionally conducted in the presence of a catalyst. Preferred catalysts are triaryl phosphorous compounds with a soluble chromium catalyst, tetra-substituted phosphonium salts, quaternary ammonium salts, carbonate salt, hydroxide salts, and salts of carboxylic acids. More preferred are tetra-substituted phosphonium salts, carbonate salts, and salts of carboxylic acids.

When a triaryl phosphorous compound is used in combination with a chromium compound, the preferred triaryl phosphorous compounds are triaryl phosphines. Preferred triaryl phosphines are triphenyl phosphine tritolyl phosphine, trixylyl phosphine, and trinaphthyl phosphine. When a triaryl phosphorous compound is used in combination with a chromium compound, the preferred the preferred chromium compounds are chromium triacetate and chromium trichloride. Among the tetra-substituted phosphonium salts, preferred are alkyltriphenylphosphonium salts, tetraarylphosphonium salts, benzyltrialkylphosphonium salts, and tetraalkylphosphonium salts; more preferred are alkyltriphenylphosphonium salts and benzyltrialkylphosphonium salts. Among alkyltriphenylphosphonium salts, preferred are ethyltriphenylphosphonium acetate/acetic acid complex, and ethyltriphenlyphosphonium iodide; more preferred is ethyltriphenylphosphonium iodide. Among tetraalkylphosphonium salts, preferred is tetrabutylphosphonium acetate/acetic acid complex. Among benzyltrialkyl phosphonium salts, preferred is benzyltrimethyl phosphonium chloride. Among tetraarylphosphonium salts, preferred is tetraphenylphosphonium bromide.

Among the quaternary ammonium salts, preferred are benzyltrimethylammonium chloride, tetramethylammonium chloride, and diphenyldimethylammonium chloride. Among the salts of carboxylic acids, preferred are sodium or potassium salts of mono-carboxylic acids; more preferred are sodium acetate, potassium acetate, sodium propionate, potassium propionate, sodium benzoate, potassium benzoate, sodium citrate, potassium citrate, sodium lactate, potassium lactate, sodium tartrate, potassium tartrate, and sodium potassium tartrate. Among the inorganic bases, preferred are sodium carbonate, potassium carbonate, sodium hydroxide, and potassium hydroxide.

The preferred catalysts for the preparation of epoxy terminated polyesters are ethyltriphenlyphosphonium iodide, benzyltrimethylammonium chloride, sodium carbonate, and sodium acetate.

When tin or titanate compounds are used in the preparation of carboxylic terminated polyester resins via the reaction of diol with dicarboxylic acid, the level preferably is in the range of 0.0001 to 0.05 wt %.

When the group —R2- has structure VI with p of 1 or greater, the compound having structure X is preferably made by one or more reaction of one or more dicarboxylic acid with one or more diol.

Embodiment (a) defined herein above is preferably made by reaction of a diepoxide with a dicarboxylic acid having the structure HOOC—R¹¹—COOH. Suitable and preferred —R¹¹— groups are the same as the suitable and preferred —R³— groups.

Embodiment (b) defined herein above is preferably made by reaction of a diepoxide with a dicarboxylic acid that is a polyester (herein called “PEb1”). PEb1 is preferably made by reacting a single dicarboxylic acid (“DAb1”) with a single diol (“DOb1”). DAb1 has the structure HOOC—R¹²—COOH. Suitable and preferred —R¹²— groups are the same as the suitable and preferred —R³— groups. DOb1 has the structure HOR¹³—OH, where —R¹³— has the structure VII. Suitable and preferred —R¹³— groups are the same as those described for structure VII. A sufficient amount of DAb1 is used so that the reaction with DOb1 will produce a polyester that is a dicarboxylic acid.

Embodiment (c) defined herein above is preferably made by reaction of a diepoxide with a dicarboxylic acid that is a polyester (herein called “PEc1”). PEc1 is preferably made by reacting a single dicarboxylic acid (“DAc1”) with an intermediate polyester (“PEc2”). DAc1 has the structure HOOC—R¹³—COOH. Suitable and preferred —R¹³— groups are the same as the suitable and preferred —R³— groups. PEc2 is preferably made by reaction of a dicarboxylic acid (“DAc2”) with one or more diol (“DOc1”). DAc2 has the structure HOOC—R¹⁴—COOH. Suitable and preferred —R¹⁴— groups are the same as the suitable and preferred —R³— groups. Preferably DAc2 is different from DAc1. DOc1 has the structure HOR¹⁵—OH, where —R¹⁵— has the structure VII. Relative amounts of DOc1 and DAc2 are used so that a significant amount of the product PEc2 is formed that has one terminal —OH group and one terminal —COOH group.

Embodiment (d) defined herein above is preferably made by reaction of a diepoxide with a dicarboxylic acid that is a polyester (herein called “PEd1”). PEd1 is preferably made by reacting a single dicarboxylic acid (“DAd1”) with an intermediate polyester (“PEd2”). DAd1 has the structure HOOC—R¹⁶—COOH. Suitable and preferred —R¹⁶— groups are the same as the suitable and preferred —R³— groups. PEd2 is preferably made by reaction of a dicarboxylic acid (“DAd2”) with one or more diol (“DOd1”). DAd2 has the structure HOOC—R¹⁷—COOH. Suitable and preferred —R¹⁷— groups are the same as the suitable and preferred —R³— groups. Preferably DAd2 is different from DAd1. DOd1 has the structure HOR¹⁸—OH, where —R¹⁸— has the structure VII. Relative amounts of DOd1 and DAd2 are used so that a significant amount of the product PEd2 is formed that has two terminal —OH groups.

Reactions between carboxylic acid groups and hydroxyl groups are preferably conducted in the presence of one or more catalyst. Preferred catalysts are tin compounds and titanate compounds. Among tin compounds, preferred are dibutyltins, tetrabutyltins, tin tetrachloride, dioctyltins, monobutyltins, and stannous tins; more preferred are hydroxybutyltin oxide, monobutyltin tris(2-ethylhexanoate), and stannous 2-ethylhexanoate. Among titanate compounds, preferred are tetraalkyltitanates; more preferred are tetra(iso-propyl) titanate and tetra(n-butyl) titanate.

For reactions between carboxylic acid groups and hydroxyl groups, when a catalyst is present, the preferred amount is 0.0001% to 0.05% by weight based on the sum of the weights of the compounds bearing carboxylic acid groups plus the compounds bearing hydroxyl groups.

The compositions of the present invention may be used for a wide variety of purposes. Preferably, a composition of the present invention is used as an ingredient in an adhesive composition that is used to bond a first substrate to a second substrate. Preferably, one or more composition of the present invention is mixed with a curative compound and optionally with a solvent; the mixture is applied to a first substrate to form a layer on the first substrate; solvent (if present) is evaporated or allowed to evaporate; a second substrate is brought into contact with the layer of the mixture; and the mixture is cured or allowed to cure.

Curative compounds are compounds that have two or more groups capable of reacting with epoxy groups. Preferred curative compounds are amino compounds. Preferred amino compounds are phenalkamines, phenalkamides, and amine-terminated amide resins. Amine-terminated amide resins are reaction products of dicarboxylic acids and diamines. For formation of amine-terminated amide resins, preferred dicarboxylic acids are dimer acids, which are the reaction products of two molecules of an unsaturated fatty acid. Unsaturated fatty acids have the structure R¹⁹—COOH, where R¹⁹— is an aliphatic group having eight or more carbon atoms one or more carbon-carbon double bond. Preferred diamines are ethylenediamine, diethylenetriamine, triethylenetriamine, tetraethylenepentamine, piperazine, aminoethylpiperazine, isophorone diamine, xylylenediamine, and mixtures thereof.

Preferred substrates are polymer films, metalized polymer films, metal foils, polymer-backed metal foils, ceramic coated polymer films, and combinations thereof.

The following are examples of the present invention.

Abbreviations used below are as follows:

-   AV=Acid Value, measured by the method of ASTM D3644-06 (American     Society for testing and Materials, Conshohocken, Pa., USA). -   OHN=Hydroxyl Number, measured by the method of ASTM E1899-08. -   Amine Value=measured by the method ASTM D2074-07 for Test Methods     for Total, Primary, Secondary, and Tertiary Amine Values of Fatty     Amines by Alternative Indicator Method. -   Visc.=Viscosity, which is measured by employing a Brookfield RV     DV-II+ Viscometer with a thermostated small sample adapter with a     spindle #27 and varying the temperature over a range of 25 to 70° C.     in increments of 5° C. and allowing the sample to stabilize at     temperature for 20 to 30 mins prior to recording viscosity.     Viscosity is reported in milliPascal*seconds (mP*s), which is equal     to centipoise. -   PO-DE1=reaction product of dipropylene oxide and epichlorhydrin,     containing a mixture of products including the following:

-   PO-DE2=reaction product of dipropylene oxide and epichlorhydrin,     containing a mixture of products including the following:

-   The DER 736, from Dow Chemical, has the flowing properties: EEW is     182.9, (SEC Analysis Mn 500, Mw 600, Mz 800, Polydispersity 1.2, Wt     Fraction ≦500 Dalton 44.6%, Wt. Fraction ≦1000 Daltons 92.0%.) -   Fascat™ 9100=hydroxybutyltin oxide, from Arkema, Inc., commercial     grade -   Unidyme™ 22=dimerized fatty acid, from Arizona Chemical, AV=192.9. -   Cardolite™ NC-541LV=phenalkamine curing agent, from Cardolite     Corporation; Amine Value is 340, Active Hydrogen Equivalent is 125. -   Polypox™ H015=Mannich base curing agent, from The Dow Chemical     Company; Amine Value of 375; Active Hydrogen Equivalent is 75. -   Polypox™ P370=polyaminoimidazoline hardener for epoxy resins, from     The Dow Chemical Company; Amine Value of 485; Active Hydrogen     Equivalent is 95. -   Epikure™ 3140=polyamide curing agent, reaction product of dimerized     fatty acid and polyamines, from Momentive; Amine Value of 375;     Active Hydrogen Equivalent of 95. -   Coex PP (75SLP)=Exxon Mobil Bicor SLP Oriented Polypropylene,     Non-Heat Sealable, thickness 19 micrometers (0.75 mils). -   Coex PP (70SPW)=Exxon Mobil Bicor SPW Coextruded Polypropylene,     thickness 18 micrometers (0.70 mils). -   PET=DuPont, Polyester, Poly(ethylene glycol-terephthalate),     thickness 23 micrometer (92 Gauge) thick polyester film. -   PE (GF-19)=Berry Plastics Corp., High slip low density polyethylene     film, thickness 25.4 micrometers (1.0 mil). -   Nylon=Honeywell Capran Emblem 1500, Biaxially Oriented Nylon 6 Film,     thickness 15 micrometers. -   PET-Met=FILMTech Inc., Metallized Polyester film, thickness 25.4     micrometers. -   OPP-Met=AET Films, Metallized Oriented Polypropylene Film, MT Film,     Heat Sealable, thickness 18 micrometers. -   Backed Foil=12 micrometer (48 Gauge) Polyester (PET) Film laminated     to 0.00035 mil Al Foil with Adcote 550/Coreactant F at 3.26 g/m²     (2.00 lbs/ream). -   PET (92LBT)=DuPont, Polyester, Poly(ethylene glycol-terephthalate),     thickness 23 micron (92 Gauge). -   Mn=number-average molecular weight -   Mw=weight-average molecular weight -   EEW=epoxy equivalent weight, which is the mass per mole of epoxy     groups -   Active Hydrogen Equivalent=mass per mole of active hydrogens; an     active hydrogen is a hydrogen atom attached to the nitrogen atom of     an amine group.

EXAMPLE 1 Polyester Preparation

Item Monomer/Intermediate Charge 1 Isophthalic Acid 1023.35 2 Diethylene Glycol 572.30 3 Ethylene Glycol 315.60 4 Fascat 9100 (Hydroxybutyltin oxide) 0.5842 5 Adipic Acid 1349.81

Charged Items 1-4 to vessel at Ambient Temperature (25-30° C.). Heated resin to 100° C. under Nitrogen with stirring. Heated resin to 225° C. and hold at 225° C., When ca.50% of theoretical water was off. Monitored AV and In-Process Viscosity. Maintained at 225° C. until AV<ca. 80. Cooled Resin to <125° C. Added Item 5; Maintained at 125-135° C. for 0.50 Hrs. Increased Temp to 225° C. and Maintained at 225° C. Monitored AV and Visc; Maintained at 225° C. until AV<ca. 200. Cooled Resin to about 150° C.; Filtered and Packaged. The final resin had the following properties: Acid Value (AV) 199, Mn 650, Mw 1250, Mz 2050, Wt. Fraction ≦500 Daltons 22.3%, Wt. Fraction ≦1000 Daltons 49.5%, Viscosity at 24.5° C. of 515,000 mPa*s.

EXAMPLE 2 Polyester Preparation

Item Ingredient Charge (g) 1 Isophthalic Acid 451.50 2 Diethylene Glycol 1081.30 3 Fascat 9100 (Hydroxybutyltin oxide) 0.5543 4 Adipic Acid 1600.78

Charged Items 1-3 to vessel at Ambient Temperature (25-30° C.). Heated resin to 100° C. under Nitrogen with stirring. Heated resin to 225° C. and held at 225° C., When ca.50% of theoretical water was off. Monitored AV and In-Process Viscosity. Maintained at 225° C. until AV<ca. 75. Cooled Resin to <125° C. Add Item 4; Maintained at 125-135° C. for 0.50 Hrs. Increased Temp to 225° C. and Maintained at 225° C.; Applied Vacuum at 400 mm as needed as to decrease AV to final target property. Monitored AV and Visc; Maintained at 225° C. until AV<ca. 155. Cooled Resin to about 150° C.; Filtered and Packaged. The final resin had the following properties: Acid Value (AV) 149.73, Mn 950, Mw 1750, Mz 2550, Wt. Fraction ≦500 Daltons 10.6%, Wt. Fraction ≦1000 Daltons 32.1%, Viscosity at 25° C. of 29500 mPa*s.

EXAMPLE 3 Polyester Preparation

Item Ingredient Charge (g) 1 Isophthalic Acid 451.94 2 Diethylene Glycol 567.80 3 Ethylene Glycol 316.34 4 Fascat 9100 (Hydroxybutyltin oxide) 0.6028 5 Adipic Acid 1601.83

Charged Items 1-4 to vessel at Ambient Temperature (25-30° C.). Heated resin to 100° C. under Nitrogen with stirring. Heated resin to 225° C. and hold at 225° C., When ca.50% of theoretical water was off. Monitored AV and In-Process Viscosity. Maintained at 225° C. until AV<ca. 75. Cooled Resin to <125° C. Added Item 5; Maintained at 125-135° C. for 0.50 Hrs. Increased Temp to 225° C. and Maintained at 225° C.; Applied Vacuum at 436 mm as needed as to decrease AV to final target property. Monitored AV and Visc; Maintained at 225° C. until AV<ca. 155. Cooled Resin to about 150° C.; Filtered and Packaged. The final resin had the following properties: Acid Value (AV) 157, Mn 750, Mw 1500, Mz 2350, Wt. Fraction ≦500 Daltons 18.1%, Wt. Fraction ≦1000 Daltons 41.3%, Viscosity at 25° C. of 22,175 mPa*s.

EXAMPLE 4 Polyester Preparation

Item Ingredient Charge (g) 1 Isophthalic Acid 940.17 2 Diethylene Glycol 572.60 3 Ethylene Glycol 316.00 4 Fascat 9100 (Hydroxybutyltin oxide) 0.3169 5 Adipic Acid 1238.98

Charged Items 1-4 to vessel at Ambient Temperature (25-30° C.). Heated resin to 100° C. under Nitrogen with stirring. Heated resin to 225° C. and hold at 225° C., When ca.50% of theoretical water was off. Monitored AV and In-Process Viscosity. Maintained at 225° C. until AV<ca. 80. Cooled Resin to <125° C. Added Item 5; Maintained at 125-135° C. for 0.50 Hrs. Increased Temp to 225° C. and Maintained at 225° C. Monitored AV and Visc; Maintained at 225° C. until AV<ca. 165. Cooled Resin to about 150° C.; Filtered and Packaged. The final resin had the following properties: Acid Value (AV) 169, Mn 950, Mw 2000, Mz 3250, Wt. Fraction ≦500 Daltons 12.5%, Wt. Fraction ≦1000 Daltons 31.0%, Viscosity at 25° C. of 221,750 mPa*s.

EXAMPLE 5 Polyester Preparation

Item Ingredient Charge (g) 1 Isophthalic Acid 908.62 2 Diethylene Glycol 1126.80 3 Fascat 9100 (Hydroxybutyltin oxide) 0.5730 4 Adipic Acid 1198.87

Charged Items 1-3 to vessel at Ambient Temperature (25-30° C.). Heated resin to 100° C. under Nitrogen with stirring. Heated resin to 225° C. and hold at 225° C., When ca.50% of theoretical water was off. Monitored AV and In-Process Viscosity. Maintained at 225° C. until AV<ca. 75. Cooled Resin to <125° C. Added Item 4; Maintained at 125-135° C. for 0.50 Hrs. Increased Temp to 225° C. and Maintained at 225° C.; Applied Vacuum at 394 mm as needed as to decrease AV to final target property. Monitored AV and Visc; Maintained at 225° C. until AV<ca. 135. Cooled Resin to about 150° C.; Filtered and Packaged. The final resin had the following properties: Acid Value (AV) 158, Mn 1150, Mw 2350, Mz 3750, Wt. Fraction ≦500 Daltons 8.5%, Wt. Fraction ≦1000 Daltons 23.6%, Viscosity at 25° C. of 175,000 mPa*s.

EXAMPLE 6 Polyester Preparation

Item Ingredient Charge (g) 1 Isophthalic Acid 942.70 2 Diethylene Glycol 654.60 3 Ethylene Glycol 362.20 4 Fascat 9100 (Hydroxybutyltin oxide) 0.3168 5 Adipic Acid 1239.19

Charged Items 1-4 to vessel at Ambient Temperature (25-30° C.). Heated resin to 100° C. under Nitrogen with stirring. Heated resin to 225° C. and hold at 225° C., When ca.50% of theoretical water was off. Monitored AV and In-Process Viscosity. Maintained at 225° C. until AV<ca. 80. Cooled Resin to <125° C. Added Item 5; Maintained at 125-135° C. for 0.50 Hrs. Increased Temp to 225° C. and Maintained at 225° C.; Applied Vacuum at 327 mm as needed as to decrease AV to final target property. Monitored AV and Visc; Maintained at 225° C. until AV<ca. 105. Cooled Resin to about 150° C.; Filtered and Packaged. The final resin had the following properties: Acid Value (AV) 98, Mn 1200, Mw 2450, Mz 3900, Wt. Fraction ≦500 Daltons 7.6%, Wt. Fraction ≦1000 Daltons 22.2%, Viscosity at 25° C. of 271,500 mPa*s.

EXAMPLE 7 Polyester Preparation

Item Ingredient Charge (g) 1 Isophthalic Acid 1158.60 2 Diethylene Glycol 720.90 3 Ethylene Glycol 398.30 4 Fascat 9100 (Hydroxybutyltin oxide) 0.4089 5 Adipic Acid 1525.85

Charged Items 1-4 to vessel at Ambient Temperature (25-30° C.). Heated resin to 100° C. under Nitrogen with stirring. Heated resin to 225° C. and hold at 225° C., When ca.50% of theoretical water was off. Monitored AV and In-Process Viscosity. Maintained at 225° C. until AV<ca. 80. Cooled Resin to <125° C. Added Item 5; Maintained at 125-135° C. for 0.50 Hrs. Increased Temp to 225° C. and Maintained at 225° C.; Applied Vacuum at 435 mm as needed as to decrease AV to final target property. Monitored AV and Visc; Maintained at 225° C. until AV<ca. 160. Cooled Resin to about 150° C.; Filtered and Packaged. The final resin had the following properties: Acid Value (AV) 153, Mn 650, Mw 1550, Mz 2650, Wt. Fraction ≦500 Daltons 19.2%, Wt. Fraction ≦1000 Daltons 42.8%, Viscosity at 25° C. of 173,750 mPa*s.

EXAMPLES 8-26 Preparations of Epoxide Terminated Polyester Resins

The preparations in Examples 8-26 were similar. Diepoxide, one or more diacid, and catalyst were charged to the reactor. Slowly Heated to 135-140° C. Maintained at 135-140° C. for ca. 0.50 Hrs and then heated to 150-155° C. and maintained at 150-155° C. for ca. 1.5 to 2 Hrs and then monitored AV and Viscosity. Maintained at 150-155° C. and monitored AV and Visc until AV<1.0. Transferred Resin and Package.

TABLE 1 Example Number: 8 9 10 11 12 13 14 Ingredient (g) DER 736 425.36 426.94 600.93 503.22 1593.93 1900.35 1900.42 Isophthalic Acid 92.92 93.00 348.83 333.00 299.80 Adipic Acid 114.00 29.24 Polyester Resin of 373.19 Ex. 1 EthylTriphenyl- 0.2486 0.2575 0.3061 0.3640 0.9532 0.7590 0.4035 phosphonium Iodide Properties EEW 544.71 482.29 472.88 771.14 487.37 416.73 411.51 Acid Value 0.11 ≦0.05 ≦0.05 ≦0.05 0.1 0.09 0.07 Mn 1000 550 1200 1950 1400 1150 1050 Mw 3800 1400 3100 4400 4400 3750 3850 Mz 9600 2850 6350 7600 10500 9500 10350 Wt. Fraction ≦500 16.8 28.8 13.0 4.8 10.1 15.6 17.4 (%) Wt. Fraction ≦1000 28.0 54.2 24.2 11.1 20.9 27.6 28.9 (%) Viscosity at 25° C. 18425 16300 3850 30400 18500 5025 6100 (mPa * s) Viscosity at 70° C. 535.0 467.5 345.0(a) 1665.0(a) 900.0(a) 365.0(a) 430.0(a) (mPa * s) (a)Viscosity at 60° C.

TABLE 2 Example Number: 15 16 17 18 19 20 Ingredient (g) DER 736 1953.00 1041.90 1002.17 1008.19 784.08 792.79 Isophthalic Acid 427.40 Polyester Resin of Ex. 2 839.04 770.69 Polyester Resin of Ex. 3 753.53 Polyester Resin of Ex. 4 655.66 Polyester Resin of Ex. 5 780.42 EthylTriphenylphosphonium 1.4638 0.5199 0.5067 Iodide Benzyltrimethylammonium 0.5630 Chloride Sodium Carbonate 0.5571 Sodium Acetate 0.5346 Properties EEW 482.29 492.53 598.00 634.90 802.95 694.54 Acid Value 0.04 0.04 0.06 0.05 0.04 0.03 Mn 1600 1500 1550 1550 2100 2000 Mw 5500 4750 4800 4700 13400 10100 Mz 14050 9000 8950 8700 44500 26900 Wt. Fraction ≦500 (%) 7.5 10.9 10.5 10.4 6.9 7.6 Wt. Fraction ≦1000 (%) 20.1 19.2 17.1 17.6 13.2 15.1 Viscosity at 25° C. (mPa * s) 18325 6512 6100 6000 23025 21800 Viscosity at 70° C. (mPa * s) 700.0(a) 320.0 342.5 345.0 1025 890.0 (a)Viscosity at 65° C.

TABLE 3 Example Number: 21 22 23 24 25 26 Ingredient (g) DER 736 775.25 763.54 679.89 600.32 1021.77 738.40 Polyester Resin of Ex. 4 520.90 Polyester Resin of Ex. 5 917.33 Polyester Resin of Ex. 6 923.08 1010.75 Polyester Resin of Ex. 7 762.94 918.60 Sodium Acetate 0.5677 0.5467 0.3591 0.5156 0.5338 0.5217 Properties EEW 847.66 759.98 656.16 1244.17 665.79 1417.64 Acid Value 0.04 <0.1 <0.1 <0.1 <0.1 <0.1 Mn 2150 1700 1400 3200 850 3050 Mw 13250 10000 7600 23450 5550 48200 Mz 39550 31500 23000 82350 17150 248300 Wt. Fraction ≦500 (%) 6.5 9.6 12.0 3.4 19.5 3.6 Wt. Fraction ≦1000 (%) 12.2 15.6 20.4 8.0 28.4 8.3 Viscosity at 25° C. 58125 38550 21875 272500 13275 776667 (mPa * s) Viscosity at 70° C. 1862 1328 805.0 6150 565.0 15000 (mPa * s)

EXAMPLE 27 Preparation of Amine Curative

Item Monomer/Intermediate Charge 1 Unidyme 22 435.94 2 Aminoethylpiperazine 242.56

Charged Item 1 and 2 to reactor, slowly heated to 200° C. Maintained at 200° C. for 2 Hr; monitor water evolution, the final resin is transferred and packaged. The final resin had the following properties: Amine Value of 217.15, Viscosity at 25° C. of 51100 mPa*s.

EXAMPLE 28 Preparation of Amine Curative

Item Monomer/Intermediate Charge 1 Amine Curative of Example 6 200.84 2 POLYPOX P370 70.01

Charged Item 1 and 2 to reactor, slowly heated to 50° C., maintain at 50° C. for 4 Hrs. The resin is transferred and packaged. The final resin had the following properties: Amine Value of 185.58, Viscosity at 25° C. of 10488 mPa*s.

EXAMPLE 29 Preparation of Amine Curative

Item Monomer/Intermediate Charge 1 Epikure 3140 252.23 2 POLYPOX P370 84.35

Charged Item 1 and 2 to reactor, slowly heated to 50° C., maintain at 50° C. for 4 Hrs. The resin is transferred and packaged. The final resin had the following properties: Amine Value of 377.45, Viscosity at 25° C. of 4825 mPa*s.

EXAMPLE 30 Preparation of Amine Curative

Item Ingredient Charge (g) 1 Unidyme 22 877.12 2 Aminoethylpiperazine 488.24

Charged Item 1 and 2 to reactor, slowly heated to 200° C. Maintained at 200° C. for 2 Hr; monitor water evolution, the final resin is transferred and packaged. The final resin had the following properties: Amine Value of 238.9, Viscosity at 25° C. of 49000 mPa*s.

EXAMPLE 31 Preparation of Amine Curative

Item Ingredient Charge (g) 1 Unidyme 22 810.77 2 Triethylenetetramine (TETA) 488.71

Charged Item 1 and 2 to reactor, slowly heated to 200° C. Maintained at 200° C. for 2 Hr; monitor water evolution, the final resin is transferred and packaged. The final resin had the following properties: Amine Value 169.64, Viscosity at 25° C. 54625 mPa*s.

The adhesion properties of the polyester-polyols and polyols were evaluated with Amine based resins using a series of laminate constructions. These two part adhesive systems were evaluated via a solvent hand casting method and laminator.

The following abbreviations are used to describe test results: as: adhesive split; ftr: film tear; fstr: film stretch; fsl: film sliver; at: adhesive transfer; sec: secondary; zip: zippery bond; pmt: partial metal transfer. Adhesion bond strengths were determined on a 15 mm wide strip of laminate on a Thwing-Albert Tensile Tester (Model QC-3A) with a 50 Newton load cell at a 10.0 cm/min rate.

Examples 32-61 were performed as follows: An epoxy terminated polyester was mixed with a curing agent at the mix ratio shown below, in ethyl acetate at 50% concentration by weight. The solution was coated on a first substrate to yield a dry coating weight of 1.6276 g/m² (1.0 lb/ream). A second substrate was applied to the dried coating and the resulting laminate was cured at room temperature (approximately 25° C.). The bond strength was examined as a function of curing time and is reported below. The “Mix ratio” is the weight ratio of epoxy resin to curing agent, expressed as 100:X. In the column labeled “laminate structure,” the first substrate is listed, followed by the second substrate.

As an example, in the table below, Example number 32 was a mixture of epoxy resin made in Example 8, mixed with curing agent POLYPDX H015, at a weight ratio of epoxy resin to curing agent of 100:13.8. The bond strength on substrates CoexPP (75SLP)/CoexPP (70SPW) at 7 days was 3.19 Newton for a width of 15 mm, and the failure mode was film tear

TABLE 4 Example Number 32 33 34 Epoxy Resin 8 8 9 from Ex. No. Curing agent POLYPOX H015 Epikure 3140 Curing Agent Ex. 27 Mix Ratio 100:13.8 100:17.4 100:45.0 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 3.19, ftr 2.05, ftr 2.26, ftr 2.02, ftr 4.84, ftr 3.83, ftr (75SLP)/ CoexPP (70SPW) CoexPP 1.65, as 1.75, as 1.16, as 2.76, ftr 6.54, ftr 6.00, ftr (75SLP)/ PE (GF-19) PET/PE 2.09, as 1.85, as 1.39, as 1.67, as 2.46, as 3.55, as (GF-19) Nylon/ 1.39, as 1.81, as 1.66, as 1.39, as 6.49, ftr 5.29, ftr PE (GF-19) PET-Met/ 1.26, as 1.35, as 1.18, as 1.19, as 2.59, ftr 2.90, ftr PE (GF-19) OPP-Met/ 1.96, as 2.06, as 2.88, as 3.55, ftr 4.16, as 4.58, as PE (GF-19) OPP-Met/ 1.85, as 2.10, as 2.49, as 2.08, ftr 1.34, as 2.61, ftr CoexPP (70SPW) Backed Foil/ 0.50, at, 0.70, at, 0.16, as 0.21, as 1.99, as 0.70, as Nylon sec sec Backed Foil/ 0.69, at, 0.83, at, 0.22, as 0.22, as 2.21, as 2.42, as PET sec sec (92LBT) Backed Foil/ 1.02, at, 1.07, at, 0.96, as 0.68, as 2.98, as 2.95, as PE (GF-19) sec sec

TABLE 5 Example Number 35 36 37 Epoxy Resin 9 9 10 from Ex. No. Curing agent POLYPOX P370 Curing Agent Curing Agent Ex. 28 Ex. 28 Mix Ratio 100:20.0 100:38.5 100:39.2 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 2.22, ftr 2.59, ftr 2.42, ftr 2.76, ftr 2.58, ftr 1.73, ftr (75SLP)/ CoexPP (70SPW) CoexPP 2.66, ftr 2.89, ftr 3.39, ftr 3.23, ftr 4.84, ftr 3.43, ftr (75SLP)/ PE (GF-19) PET/PE 2.38, as 2.36, as 2.73, as 2.30, as 1.40, as 2.00, as (GF-19) Nylon/ 2.81, ftr 3.09, ftr 3.95, ftr 2.98, ftr 2.13, as 2.16, as PE (GF-19) PET-Met/ 1.17, as 1.85, as 2.46, as 1.90, ftr 1.25, as 1.22, as PE (GF-19) OPP-Met/ 1.21, as 2.03, as 2.57, as 3.08, as 2.95, as 3.46, as PE (GF-19) OPP-Met/ 1.14, as 1.21, as 2.47, as 2.32, ftr 1.43, as 1.73, as CoexPP (70SPW) Backed Foil/ 0.25, as 0.00, as 0.94, as 0.56, as 0.46, as 0.09, as Nylon Backed Foil/ 0.15, as 0.00, as 0.97, as 0.36, as 0.28, as 0.16, as PET (92LBT) Backed Foil/ 0.42, as 0.57, as 2.30, as 2.23, as 0.78, as 1.12, as PE (GF-19)

TABLE 6 Example Number 38 39 40 Epoxy Resin 10 11 11 from Ex. No. Curing agent Curing Agent Curing Agent Curing Agent Ex. 27 Ex. 28 Ex. 27 Mix Ratio 100:45.9 100:24.1 100:28.2 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 2.45, ftr 1.82, ftr 2.38, as 2.52, ftr 2.37, as 2.11, as (75SLP)/ CoexPP (70SPW) CoexPP 3.11, as 3.29, ftr 2.34, as 2.17, as 2.17, as 2.00, as (75SLP)/ PE (GF-19) PET/PE 2.18, as 2.35, as 3.31, as 2.63, as 2.19, as 2.76, as (GF-19) Nylon/ 1.72, as 2.23, as 2.28, as 2.59, as 3.63, as 2.86, as PE (GF-19) PET-Met/ 1.37, as 1.30, as 1.59, as 2.29, as 4.40, as 3.82, as PE (GF-19) OPP-Met/ 2.42, as 3.11, as 2.50, as 3.00, as 2.25, as 3.06, as PE (GF-19) OPP-Met/ 2.88, as 2.86, as 2.20, as 2.56, as 2.75, as 1.80, as CoexPP (70SPW) Backed Foil/ 1.23, as 1.29, as 0.00, as 0.71, as 1.06, as 0.61, as Nylon Backed Foil/ 0.52, as 1.21, as 1.31, as 0.97, as 1.27, as 1.23, as PET (92LBT) Backed Foil/ 1.20, as 1.46, as 2.18, as 1.75, as 2.34, as 2.11, as PE (GF-19)

TABLE 7 Example Number 41 42 43 Epoxy Resin 13 13 16 from Ex. No. Curing agent Epikure 3140 Curing Agent Ex Curing Agent Ex 27 30 Mix Ratio 100:22.8 100:22.8 100:48.4 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 3.11, ftr 3.59, ftr 1.52, as 2.37, ftr 1.88, ftr 2.27, ftr (75SLP)/ CoexPP (70SPW) CoexPP 2.23, as 2.46, as 1.93, as 1.99, as 3.52, as 2.99, as (75SLP)/ PE (GF-19) PET/PE 2.08, as 3.02, as 2.17, as 2.31, as 2.84, as 3.51, as (GF-19) Nylon/ 1.39, as 1.64, as 1.54, as 1.45, as 4.97, as 1.92, as PE (GF-19) PET-Met/ 0.38, as 0.40, as 2.12, as 0.25, as 0.87, as 1.33, as PE (GF-19) OPP-Met/ 0.52, as 0.57, as 0.68, as 0.38, as 1.06, as 1.18, as PE (GF-19) OPP-Met/ 0.48, as 0.70, as 1.09, as 0.38, as 1.12, as 0.97, as CoexPP (70SPW) Backed Foil/ 0.83, as 0.69, as 0.91, as 0.46, as 1.89, as 1.62, as Nylon Backed Foil/ 0.36, as 0.37, as 0.93, as 0.25, as 1.51, as 1.91, as PET (92LBT) Backed Foil/ 1.33, as 1.92, as 1.72, as 1.65, as 2.51, as 2.05, as PE (GF-19)

TABLE 8 Example Number 44 45 46 Epoxy Resin 16 17 17 from Ex. No. Curing agent Curing Agent Curing Agent Curing Agent Ex 31 Ex 30 Ex 31 Mix Ratio 100:34.4 100:39.9 100:28.4 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 1.87, ftr 2.95, ftr 1.93, as 1.05, as 1.70, ftr 1.40, ftr (75SLP)/ CoexPP (70SPW) CoexPP 3.84, ftr 4.03, ftr 1.55, as 0.73, as 1.99, as 2.18, as (75SLP)/ PE (GF-19) PET/PE 1.24, as 0.91, as 1.67, as 1.64, as 1.36, as 1.52, as (GF-19) Nylon/ 1.65, as 1.71, as 1.36, as 1.37, as 0.31, as 1.40, as PE (GF-19) PET-Met/ 0.43, as 0.33, as 0.97, as 1.17, as 0.40, as 0.61, as PE (GF-19) OPP-Met/ 0.58, as 0.39, as 0.89, as 0.75, as 0.42, as 0.77, as PE (GF-19) OPP-Met/ 0.49, as 0.64, as 1.10, as 0.98, as 0.49, as 0.42, as CoexPP (70SPW) Backed Foil/ 0.76, as 0.69, as 0.36, as 0.94, as 0.27, as 0.32, as Nylon Backed Foil/ 0.90, as 0.17, as 0.46, as 0.79, as 0.26, as 0.22, as PET (92LBT) Backed Foil/ 1.18, as 1.21, as 1.55, as 1.89, as 0.77, as 1.31, as PE (GF-19)

TABLE 9 Example Number 47 48 49 Epoxy Resin 18 18 19 from Ex. No. Curing agent Curing Agent Curing Agent Curing Agent Ex 30 Ex 31 Ex 30 Mix Ratio 100:37.6 100:26.7 100:29.7 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 1.42, as 1.03, as 1.79, as 1.77, ftr 1.11, as 1.06, as (75SLP)/ CoexPP (70SPW) CoexPP 0.93, as 1.41, as 1.65, as 2.10, as 1.10, as 1.54, as (75SLP)/ PE (GF-19) PET/PE 1.34, as 1.60, as 1.59, as 1.41, as 1.84, as 1.74, as (GF-19) Nylon/ 0.88, as 1.30, as 1.42, as 1.20, as 2.11, as 1.58, as PE (GF-19) PET-Met/ 0.94, as 0.50, as 0.48, as 0.43, as 0.69, as 1.08, as PE (GF-19) OPP-Met/ 0.29, as 0.37, as 0.38, as 0.59, as 0.80, as 0.72, as PE (GF-19) OPP-Met/ 0.41, as 0.62, as 0.48, as 0.46, as 0.87, as 1.26, as CoexPP (70SPW) Backed Foil/ 1.18, as 1.85, as 0.66, as 0.79, as 1.13, as 1.83, as Nylon Backed Foil/ 0.68, as 1.17, as 0.64, as 0.73, as 0.59, as 1.41, as PET (92LBT) Backed Foil/ 0.81, as 0.98, as 1.05, as 0.97, as 1.41, as 2.03, as PE (GF-19)

TABLE 10 Example Number 50 51 52 Epoxy Resin 19 15 20 from Ex. No. Curing agent Curing Agent Curing Agent Curing Agent Ex 31 Ex 31 Ex 30 Mix Ratio 100:21.1 100:35.2 100:34.3 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 1.10, as 1.23, as 1.65, ftr 2.35, ftr 0.30, as 0.30, as (75SLP)/ CoexPP (70SPW) CoexPP 2.13, ftr 1.54, as 3.09, ftr 2.06, ftr 0.42, as 0.42, as (75SLP)/ PE (GF-19) PET/PE 1.39, as 1.37, as 2.31, as 2.28, as 0.37, as 0.37, as (GF-19) Nylon/ 1.23, as 1.28, as 1.16, as 1.71, as 0.23, as 0.23, as PE (GF-19) PET-Met/ 0.54, as 0.71, as 0.25, as 0.33, as 0.58, as 0.58, as PE (GF-19) OPP-Met/ 0.79, as 0.86, as 0.48, as 0.54, as 0.64, as 0.64, as PE (GF-19) OPP-Met/ 0.76, as 0.79, as 0.47, as 0.57, as 0.35, as 0.35, as CoexPP (70SPW) Backed Foil/ 0.90, as 0.81, as 0.63, as 0.60, as 0.76, as 0.76, as Nylon Backed Foil/ 0.80, as 0.70, as 0.35, as 0.33, as 0.52, as 0.52, as PET (92LBT) Backed Foil/ 1.00, as 1.06, as 0.85, as 1.22, as 0.90, as 0.90, as PE (GF-19)

TABLE 11 Example Number 53 54 55 Epoxy Resin 20 22 22 from Ex. No. Curing agent Curing Agent Curing Agent Curing Agent Ex 31 Ex 30 Ex 31 Mix Ratio 100:24.4 100:31.4 100:22.3 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 0.94, as 2.29, ftr 0.52, as 0.82, as 0.92, as 1.96, fsl (75SLP)/ CoexPP (70SPW) CoexPP 1.25, as 2.57, fsl 0.82, as 1.01, as 1.15, as 1.82, as (75SLP)/ PE (GF-19) PET/PE 1.56, as 1.87, as 0.76, as 0.87, as 1.11, as 1.45, as (GF-19) Nylon/ 1.11, as 1.31, as 0.67, as 0.83, as 0.86, as 1.46, as PE (GF-19) PET-Met/ 0.29, as 0.29, as 0.72, as 0.62, as 0.28, as 0.35, as PE (GF-19) OPP-Met/ 0.52, as 0.47, as 0.92, as 0.80, as 0.46, as 0.47, as PE (GF-19) OPP-Met/ 0.50, as 0.51, as 0.79, as 0.80, as 0.49, as 0.54, as CoexPP (70SPW) Backed Foil/ 0.72, as 0.80, as 1.04, as 1.08, as 0.86, as 0.90, as Nylon Backed Foil/ 0.36, as 0.42, as 1.05, as 1.23, as 0.53, as 0.52, as PET (92LBT) Backed Foil/ 0.89, as 0.91, as 0.94, as 0.85, as 0.87, as 1.05, as PE (GF-19)

TABLE 12 Example Number 56 57 58 Epoxy Resin 23 23 25 from Ex. No. Curing agent Curing Agent Curing Agent Curing Agent Ex 30 Ex 31 Ex 30 Mix Ratio 100:36.3 100:25.9 100:37.6 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 1.26, as 1.14, as 1.09, as 2.06, fsl 0.54, as 0.90, as (75SLP)/ CoexPP (70SPW) CoexPP 1.63, as 1.35, as 1.68, as 3.27, ftr 1.49, as 1.70, as (75SLP)/ PE (GF-19) PET/PE 1.60, as 1.41, as 1.25, as 1.77, as 1.19, as 0.72, as (GF-19) Nylon/ 1.15, as 1.64, as 1.61, as 2.56, as 1.17, as 1.19, as PE (GF-19) PET-Met/ 0.50, as 0.61, as 0.25, as 0.36, as 0.56, as 0.52, as PE (GF-19) OPP-Met/ 0.71, as 0.76, as 0.44, as 0.49, as 0.60, as 0.64, as PE (GF-19) OPP-Met/ 0.73, as 0.85, as 0.43, as 0.51, as 0.69, as 0.51, as CoexPP (70SPW) Backed Foil/ 1.42, as 1.14, as 0.67, as 0.79, as 0.83, as 1.14, as Nylon Backed Foil/ 1.12, as 1.16, as 0.31, as 0.44, as 0.52, as 0.80, as PET (92LBT) Backed Foil/ 1.11, as 1.12, as 0.85, as 1.10, as 0.94, as 1.03, as PE (GF-19)

TABLE 13 Example Number 59 60 61 Epoxy Resin 25 15 15 from Ex. No. Curing agent Curing Agent PRIAMINE 1071 JEFFAMINE Ex 31 D400 Mix Ratio 100:26.7 100:40.2 100:23.8 Laminate Bond Strength (N/15 mm) Structure 7 Days 14 Days 7 Days 14 Days 7 Days 14 Days CoexPP 1.46, ftr 2.28, ftr 1.87, ftr 2.91, ftr 1.13, as 0.89, as (75SLP)/ CoexPP (70SPW) CoexPP 1.13, as 1.33, as 2.62, ftr 2.56, ftr 1.36, as 2.07, as (75SLP)/ PE (GF-19) PET/PE 1.23, as 1.79, as 0.78, as 1.07, as 1.29, as 1.26, as (GF-19) Nylon/ 0.83, as 0.30, as 1.45, as 1.49, ftr 1.04, as 0.67, as PE (GF-19) PET-Met/ 0.25, as 0.00, as 0.23, as 0.00, as 0.00, as 0.17, as PE (GF-19) OPP-Met/ 0.41, as 0.22, as 0.51, as 0.22, as 0.00, as 0.27, as PE (GF-19) OPP-Met/ 0.41, as 0.42, as 0.39, as 0.24, as 0.38, as 0.25, as CoexPP (70SPW) Backed Foil/ 0.49, as 0.66, as 0.00, as 0.00, as 0.00, as 0.00, as Nylon Backed Foil/ 0.00, as 0.00, as 0.00, as 0.00, as 0.00, as 0.00, as PET (92LBT) Backed Foil/ 0.78, as 0.75, as 0.74, as 0.65, as 0.27, as 0.78, as PE (GF-19) 

1. An epoxy terminated polyester having the structure

wherein R¹— is

G- is

j is 0 to 5, —R²— is a divalent organic group, —R²¹— is a divalent alkyl group, and —R²²— is a divalent alkyl group.
 2. The polyester of claim 1, wherein said —R²¹— has 3 carbon atoms and every —R²²— has 3 carbon atoms.
 3. The polyester of claim 2, wherein at least one —R²²— has the structure selected from


4. The polyester of claim 1, wherein said —R²— is

wherein said —R³— and —R⁴— and —R⁵— is each independently a divalent organic group, and wherein said p is 0 to
 20. 5. The polyester of claim 4, wherein said —R³— is either —(CH₂)_(q)— or

wherein q is 1 to
 8. 6. The polyester of claim 4, wherein said —R⁴— is either —CH₂—CH₂— or —CH₂—CH₂—O—CH₂—CH₂—. 